The presence of acicular ferrite (AF) in the microstructure of weld bead, in a specified range of values, increase considerably the toughness of welded joints. The present paper, for that reason, study the relationship between the acicular ferrite quantity in the deposited metal and the oxygen present in the active gas mixture of CO2+O2, during the execution of butt welded joints with straight edges, in low carbon steels with consumable electrode and gas protection (GMAW) in invariable conditions of process parameters (welding current, arc voltage, welding speed, electrode extension, and gas flow). The graphic relation between the acicular ferrite and the oxygen content was established, as result of the research work.

La presencia de ferrita acicular (FA) en la microestructura del cordón de soldadura, dentro de determinado rango de valores, eleva considerablemente la tenacidad de las uniones soldadas. Es por ello, que el presente trabajo trata sobre un estudio que relaciona la cantidad de ferrita acicular en el cordón en función del contenido de oxígeno presente en la mezcla activa CO2+O2, durante la realización de uniones soldadas de bordes rectos en aceros de bajo carbono con el proceso con electrodo fusible y protección gaseosa (GMAW) en condiciones invariables de parámetros de proceso (corriente de soldadura, voltaje de arco, velocidad de soldadura, longitud libre y flujo de gas protector). Como resultado del trabajo se estableció la relación gráfica existente entre la ferrita acicular y el contenido de oxígeno en la mezcla.